Usporedna tablica sličnih vrsta nehrđajućeg čelika

 

 

EN 10 027-2 EN 10 027-1 AISI
1.4000 X6Cr 13 410S
1.4002 X6CrAL 13 405
1.4006 X12Cr 13 410
1.4016 X6Cr 17 430
1.4021 X20Cr 13 420
1.4057 X17CrNi 16-2 431
1.4104 X14CrMoS17 430F
1.4109 X70CrMo 15 440A
1.4112 X90CrMoV 18 440B
1.4113 X6CrMo 17-1 434
1.4125 X105CrMo 17 440C
1.4301 X5CrNi18-10 304
1.4303 X4CrNi18-12 305
1.4305 X8CrNi19-9 303
1.4306 X2CrNi19-11 304L
1.4307 X2CrNi18-9 304L
1.4310 X10CrNi18-8 301
1.4311 X2CrNiN18-10 304LN
1.4313 X3CrNiMo13-4
1.4401 X5CrNiMo17-12-2 316
1.4404 X2CrNiMo17-12-2 316L
1.4435 X5CrNiMo18-14-3 316L
1.4436 X3CrNiMo17-13-3 316
1.4438 X2CrNiMo18-15-4 317L
1.4439 X2CrNiMoN17-13-5 317LMN
1.4449 X5CrNiMo17-13 317
1.4460 X3CrMoN27-5-2 329
1.4462 X2CrNiMoN22-5-3 318LN
1.4510 X3CrTi 17 439
1.4512 X2CrTi 12 409
1.4541 X6CrNiTi18-10 321
1.4542 X5CrNiCuNb16-4 630
1.4550 X6CrNiNb18-10 347
1.4571 X5CrNiMoTi17-12-3 316Ti

 

Oznake V2A i V4A

U poduzeću Krupp je još 1912. godine po prvi puta proizvedena legura čelika sa ciljanom kombinacijom kroma i nikla. (X12CrNi18-8 ili 1.4300 -  danas se više ne proizvodi)  Za ondašnje vrijeme to bio optimum zaštite od korozije i dobrih mehaničkih svojstava. V2A je značilo Versuchsschmelze 2 Austenit, prevedeno sa njemačkog - pokusna smjesa 2 austenit. Broj 2 je označavao kombinaciju CrNi 18-8. Kod V4A, broj 4 je označavao još plus 2% molibdena - kombinacija CrNiMo.
 
Danas se pod V2A obično podrazumijevaju materijali 1.4301 (najčešće), 1.4541, 1.4550, a pod V4A materijali 1.4401 (najčešće), 1.4571 i 1.4580. Isto tako su i malo prilagođeni nazivi tako da se danas puno ćešće koristi A2 za V2A i A4 za V2A. U upotrebi ali osjetno manjoj još se nalaze oznake V1A, V3A i V5A.